Especially where brass parts are exposed to grinding movements as well as to wear stress, where tenacity, surface quality, thermal conductivity and wear resistance are required, the BMOTION high-tensile brasses of Diehl Metall fit perfectly.
Due to the addition of appropriate elements such as: Aluminium, Manganese, Iron, Silicon, Nickel or Tin, the material properties of the brass can be modified effectively. These additions affect the microstructure of our special brasses. This leads to an increase in the resistance and hardness of the material. They also form intermetallic compounds that are stored as hard microstructural constituents in the material matrix and increase the wear resistance.
Alexander Dehnelt
Sales Director
Diehl Metall Messing
Tel: +49 911 5704-347
Mail: Alexander.Dehnelt@diehl.com
Marcus Hiemeyer
Sales Director Export
Diehl Metall Messing
Tel: +49 911 5704-191
Mail: Marcus.Hiemeyer@diehl.com
| Cu % | Al % | Mn % | Si % | Fe % | Pb % | Ni % | Cr % | Sn % | EN alloy | EN nr. | CDA |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 356 | 58 | 2,0 | 2,5 | 1,1 | 0,2 | -- | -- | -- | -- | -- | -- |
| 357 | 60 | 1,6 | 2 | 0,7 | -- | 0,5 | -- | -- | -- | -- | -- |
| 358 | 57 | 1 | 1,5 | 0,5 | 0,5 | 0,5 | -- | -- | -- | -- | -- |
| 362 | 61 | -- | 2,5 | 0,8 | -- | -- | -- | -- | -- | -- | -- |
| 430 PbF | 76 | -- | -- | 3 | -- | -- | -- | -- | -- | -- | -- |
| 451 | 59 | -- | 0,5 | -- | -- | 1,5 | -- | -- | -- | CuZn40Mn1Pb1 | CW720R |
| 452 | 58 | 1,5 | 2 | 0,8 | 0,5 | 0,5 | -- | -- | 0,3 | CuZn37Mn3Al2PbSi | CW713R |
| 453 | 58 | 1 | 1,5 | 0,5 | 0,5 | 0,5 | -- | -- | -- | -- | -- |
| 454 | 59 | 1,5 | 1,8 | 0,4 | -- | 0,5 | 1 | -- | -- | CuZn37Mn3Al2PbSi | CW713R |
| 455 | 58 | 1,5 | 1,6 | 0,6 | 0,7 | 0,5 | -- | -- | 0,4 | -- | -- |
| 458 | 58 | 1,5 | 2 | 0,5 | 0,3 | 0,5 | -- | -- | -- | CuZn37Mn3Al2PbSi | Cw713R |
| 460 | 58 | 1 | 2 | -- | -- | 0,7 | 2,5 | -- | -- | CuZn35Ni3Mn2AlPb | -- |
| 466 | 65 | 6 | 4 | -- | 3 | 0,5 | -- | -- | -- | CuZn23Al6Mn4Fe3Pb | CW704R |
| 468 | 67 | -- | -- | 1 | -- | -- | -- | -- | -- | CuZn31Si1 | CW708R |
| 469 | 67 | -- | -- | 1 | -- | 0,2 | -- | -- | -- | CuZn31Si1 | CW708R |
| 470 HT | 70 | 5 | 7 | 2 | 1 | 1 | -- | -- | -- | -- | -- |
| 471 | 61 | 2,5 | 3,5 | 0,6 | 0,5 | -- | 0,8 | -- | -- | -- | -- |
| 474 HT | 70 | 5 | 7 | 2 | 1 | -- | -- | -- | -- | -- | -- |
| 479 | 62 | 3 | 3 | 1 | -- | -- | 0,4 | 0,2 | -- | -- | -- |
| 488 | 55 | 4 | -- | 2 | 0,7 | -- | 7 | -- | -- | -- | -- |
| 489 | 66 | 5 | 7 | 2 | 1 | 0,5 | -- | -- | -- | -- | -- |
| 490 | 46 | 0,2 | -- | 4 | -- | 0,5 | 14 | -- | -- | -- | -- |